| NAME |
DESCRIPTION
|
EPOXY
VALUE eg/kg
|
VISCOSITY
AT 25OC cps
|
SOFTENING
POINT DEG. C. (2)
|
COMMENTS
|
| LAPOX
P-3 |
SOLID
|
2.15-2.22
|
160-190
|
60-72
|
Recommended
with amine adducts and polyaminoamide curing agents
for solvent containing cold-curing chemical resistant
coatings and marine paints. |
| LAPOX
P-101 |
SOLVENT
CUT
|
1.90-2.2(100%
RESIN)
|
6000-12000
|
--
|
75%
solvent cut of LAPOX P-3 in Xylene |
| LAPOX
P-4 |
SOLID
|
1.12-1.20
|
550-700
|
90-102
|
Recommended
for esterification with fatty acids for enamels and
exterior coatings of cans and tubes. |
| LAPOX
P-10 |
SOLID
|
1.08-1.18
|
430-550
|
90-100
|
Special
resin for esterification to formulate water based
systems for anodic electrodeposition. |
| LAPOX
P-5 |
SOLID
|
0.53-0.59
|
1800-2600
|
110-120
|
Recommended
for cross linking with amino and phenolic resins as
stoving lacquers for the internal coating of cans and
tubes. |
| LAPOX
P-6 |
SOLID
|
0.34-0.42
|
5000-10000
|
125-140
|
Higher
molecular weight resin recommended for cross inking
with amino and phenolic resins as stoving lacquers for
internal coatings of cans and tubes. |
| LAPOX
P-62 |
SOLID
|
1.33-1.40
|
500-600
|
95-101
|
Recommended
for powder coating formulations. |
| LAPOX
P-106 |
SOLID
|
1.00-1.20
|
450-600
|
85-95
|
Formulated
type 4 resin used in combination with carboxyl
terminated polyester resins for formulation of powder
coatings with good flow properties. |
| LAPOX
P-71 |
SOLID
|
1.68-1.75
|
280-340
|
75-85
|
Higher
melting point resin used in cold-curing lacquers,
suitable for improving the flow properties &
chemical resistance of epoxy powder coatings. |
| LAPOX
P-44 |
PASTE
|
4.30-4.8
|
13000-23000
|
--
|
Formulated
white pigmented epoxy resin used in combination with
hardener K-92 for solvent free, room temperature
curing chemical resistant linings. |
| LAPOX
P-91 |
LIQUID
|
3.50-4.20
|
16000-22000
|
--
|
Formulated
epoxy resin recommended in combination with hardener
K-91 for making knifing putties, curable at room
temperature. |
| LAPOX
P-103 |
LIQUID
|
5.26-5.38
|
12000-14000
|
MAX 2
|
Special
basic resin with negligible ionic impurities used to
formulate cationic electrodeposition primers. |
| LAPOX
P-98 |
40%
SOLUTION IN MEK
|
MAX
0.15(Based on 100% Resin)
|
600-1100
|
MAX 3
|
Very
high mol. wt. resin used to formulate zinc rich
primers with or without a hardener. Can also be used
as a Polyol in polyurethane coatings. |